Built-in Antistatic PP for Thermoforming
Yuanle supplies polypropylene sheet with antistatic properties incorporated into the material rather than applied as a surface coating.
- Long-lasting antistatic performance: 3 years for the specified grade and conditions.
- Performance after forming: built-in antistatic functionality is maintained in stretched areas after thermoforming.
- Electrical selection: confirm the selected grade, target range, measurement method and conditioning requirements.
Electrical range: 104–1010. Confirm the grade-specific measurement method, unit and conditioning requirements.
Built-in versus Surface-Coated Antistatic PP
Surface coatings may lose electrical performance where substantial stretching disrupts the treated surface. Built-in antistatic PP incorporates the functionality into the material. Compare actual grades under the same forming and measurement conditions.
Validate your formed tray, including highly stretched corners and sidewalls, against your required electrical specification.
Request a Quote or Forming Sample
Send your sheet thickness and width, electrical target, forming depth, application and estimated quantity.
Request a Quote | Request a PP Sample | Request Technical Data
Physical Property Reference
Request grade-specific technical data to confirm the reference ranges below for your application.
| Property Category | Property | Test Standard | Typical Value / Range | Unit |
| Physical Properties | Density | ASTM D792 | 0.90 – 0.91 | g/cm³ |
| Melt Flow Rate (MFR) (230°C/2.16 kg) | ASTM D1238 | 0.3 – 30 | g/10 min | |
| Mechanical Properties | Tensile Strength at Yield | ASTM D638 | 26.0 – 29.0 | MPa |
| Tensile Modulus | ASTM D638 | 993 – 1220 | MPa | |
| Elongation at Break | ASTM D638 | >200 | % | |
| Flexural Modulus | ASTM D790 | 1,100 – 1,640 | MPa | |
| Izod Impact, Notched (23°C) | ASTM D256 | 15 – No Break | J/m | |
| Hardness, Rockwell | ASTM D785 | R75 – R94 | — | |
| Thermal Properties | Deflection Temperature Under Load (DTUL) @ 0.45 MPa (66 psi) | ASTM D648 | 76 – 105 | °C |
| Deflection Temperature Under Load (DTUL) @ 1.8 MPa (264 psi) | ASTM D648 | ~50 – 60 | °C | |
| Melting Point | DSC | 160 – 165 | °C |